SABIC Innovative Plastics Ultem 2412EPR PEI 物性表
| 比重 | 1.56 g/cc | 1.56 g/cc | ASTM D 792 |
| 密度 | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 |
| 平衡吸湿 | 0.40 % | 0.40 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.80 % @Temperature 23.0 °C | 0.80 % @Temperature 73.4 °F | ISO 62 |
| 线性成型收缩率,Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | on tensile bar; SABIC Method |
| 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm | 0.0020 - 0.0040 in/in @Thickness 0.126 in | SABIC Method | |
| 线性成型收缩率，横向 | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm | SABIC Method | |
| 熔体流动速率 | 9.5 g/10 min @Load 6.60 kg, Temperature 337 °C | 9.5 g/10 min @Load 14.6 lb, Temperature 639 °F | ASTM D 1238 |
| 13 g/10 min @Load 5.00 kg, Temperature 360 °C | 13 g/10 min @Load 11.0 lb, Temperature 680 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 硬度，H358/30 | 165 MPa | 23900 psi | ISO 2039-1 |
| 抗张强度(断裂) | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 |
| 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D 638 | |
| 抗张强度(屈服) | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 |
| 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D 638 | |
| 伸长率 (断裂) | 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D 638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| 屈服伸长率 | 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D 638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| 拉伸模量 | 9.80 GPa | 1420 ksi | 5 mm/min; ASTM D 638 |
| 10.1 GPa | 1460 ksi | 1 mm/min; ISO 527 | |
| 弯曲强度 | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
| 148 MPa | 21500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 弯曲模量 | 6.91 GPa | 1000 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 7.20 GPa | 1040 ksi | 2 mm/min; ISO 178 | |
| 悬壁梁缺口冲击强度 | 0.370 J/cm @Temperature 23.0 °C | 0.693 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| 悬壁梁无缺口冲击强度 | 4.43 J/cm @Temperature 23.0 °C | 8.30 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| 悬壁梁缺口冲击强度 | 5.00 kJ/m² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| 悬壁梁无缺口冲击强度 | 25.0 kJ/m² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| 25.0 kJ/m² @Temperature -30.0 °C | 11.9 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |
| 简支梁无缺口冲击强度 | 2.00 J/cm² @Temperature -30.0 °C | 9.52 ft-lb/in² @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 2.10 J/cm² @Temperature 23.0 °C | 9.99 ft-lb/in² @Temperature 73.4 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 0.500 J/cm² @Temperature 23.0 °C | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| 0.500 J/cm² @Temperature -30.0 °C | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | ||
| 冲击试验 | 16.0 J @Temperature 23.0 °C | 11.8 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |