(聚醚)TPU 美国Lubrizol 2103-70A
![](http://img4.11467.com/2021/02-24/1131810999.jpg)
Estane® 2103-70A TPU 物性表
黄卡编号 | E106426-100187491 |
特性 | High Moisture Vapor Transmission |
形式 | 粒子 |
加工方法 | 注射成型 |
比重 | 1.06 | g/cm³ | ASTM D792 |
熔流率(熔体流动速率) (224°C/8.7 kg) | 11 | g/10 min | ASTM D1238 |
收缩率 | ASTM D955 | ||
流动 | -0.30 到 0.80 | % | ASTM D955 |
横向流动 | 0.40 到 0.50 | % | ASTM D955 |
肖氏硬度 (邵氏 A) | 72 | ASTM D2240 |
泰伯耐磨性 (1000 g, H-22 转轮) | 3.00 | mg | ASTM D1044 |
拉伸应力 | ASTM D412 | ||
50%应变, 3.20 mm | 2.10 | MPa | ASTM D412 |
100 应变, 3.20 mm | 3.00 | MPa | ASTM D412 |
300%应变, 3.20 mm | 5.20 | MPa | ASTM D412 |
抗张强度 (断裂, 3.20 mm) | 24.7 | MPa | ASTM D412 |
伸长率 (断裂, 3.20 mm) | 730 | % | ASTM D412 |
断裂伸长率 (3.20 mm) | 50 | % | ASTM D412 |
撕裂强度 1(3.20 mm) | 66.5 | kN/m | ASTM D624 |
压缩变形 | ASTM D395B | ||
25°C, 22 hr | 25 | % | ASTM D395B |
70°C, 22 hr | 75 | % | ASTM D395B |
玻璃转化温度 | -69.0 | °C | DSC |
维卡软化温度 | 75.6 | °C | ASTM D1525 2 |
线形热膨胀系数 - 流动 | 1.8E-4 | cm/cm/°C | ASTM D696 |
干燥温度 | 82.0 到 93.0 | °C | |
加工(熔体)温度 | 193 到 210 | °C | |
模具温度 | 16.0 到 60.0 | °C |
Air Dew Point: <-40°C |
干燥温度 | 82.0 到 93.0 | °C | |
熔体温度 | 188 到 204 | °C |
展开全文