可喷涂 PPO 沙伯基础(美国) GTX8720 74709
SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA 物性表
| 比重 | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| 密度 | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| 水分吸收 | 0.500 % | 0.500 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 4.0 % | 4.0 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0026 - 0.0030 cm/cm @Thickness 3.20 mm | 0.0026 - 0.0030 in/in @Thickness 0.126 in | SABIC Method |
| 线性成型收缩率，横向 | 0.0072 - 0.0085 cm/cm @Thickness 3.20 mm | 0.0072 - 0.0085 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 8.6 g/10 min @Load 5.00 kg, Temperature 280 °C | 8.6 g/10 min @Load 11.0 lb, Temperature 536 °F | ASTM D1238 |
| 化合物熔体指数 | 7.0 g/10 min @Load 5.00 kg, Temperature 280 °C | 7.0 g/10 min @Load 11.0 lb, Temperature 536 °F | MVR [cm^3/10 min]; ISO 1133 |
| 抗张强度(断裂) | 140 MPa | 20300 psi | Type I, 5 mm/min; ASTM D638 |
| 140 MPa | 20300 psi | 5 mm/min; ISO 527 | |
| 抗张强度(屈服) | 140 MPa | 20300 psi | Type I, 5 mm/min; ASTM D638 |
| 140 MPa | 20300 psi | 5 mm/min; ISO 527 | |
| 伸长率 (断裂) | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 5 mm/min; ISO 527 | |
| 屈服伸长率 | 3.1 % | 3.1 % | Type I, 5 mm/min; ASTM D638 |
| 3.1 % | 3.1 % | 5 mm/min; ISO 527 | |
| 拉伸模量 | 7.00 GPa | 1020 ksi | 5 mm/min; ASTM D638 |
| 7.00 GPa | 1020 ksi | 1 mm/min; ISO 527 | |
| 弯曲强度 | 200 MPa | 29000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 200 MPa | 29000 psi | 2 mm/min; ISO 178 | |
| 弯曲模量 | 6.60 GPa | 957 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 6.60 GPa | 957 ksi | 2 mm/min; ISO 178 | |
| 悬壁梁缺口冲击强度 | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| 0.600 J/cm @Temperature -30.0 °C | 1.12 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A | |
| 8.00 kJ/m² @Temperature -30.0 °C | 3.81 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| 简支梁缺口冲击强度 | 1.10 J/cm² | 5.23 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 落锤总能量 | 17.0 J @Temperature 23.0 °C | 12.5 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| 体积电阻率 | 1000 - 10000 ohm-cm | 1000 - 10000 ohm-cm | SABIC Method |
| 线形热膨胀系数 - 流动 | 23.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 12.8 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 23.0 µm/m-°C @Temperature -40.0 - 40.0 °C | ISO 11359-2 | ||
| 线性热膨胀系数,横向流动 | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 44.4 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C | ISO 11359-2 | ||
| 载荷下热变形温度(0.46 MPa) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 215 °C @Thickness 3.20 mm | 419 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 维卡软化温度 | 215 °C | 419 °F | Rate B/50; ASTM D1525 |
| 215 °C | 419 °F | Rate B/50; ISO 306 | |
| 225 °C | 437 °F | Rate B/120; ISO 306 |