FLEX NORYL™PPO 沙伯基础PPOHMC202M
沙特基础FLEX NORYL™PPOHMC202M
>PPO-FR< 阻燃等级: V-1 缺口冲击: 4.28 kJ/m² 热变形温度: 181 °C 符合规定: UL
产品说明：
DATA ON BK1005 ONLY.
物性信息：
| 比重 | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| 线性成型收缩率,Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm | 0.0010 - 0.0030 in/in @Thickness 0.126 in | SABIC Method |
| 线性成型收缩率，横向 | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0060 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 7.6 g/10 min @Load 5.00 kg, Temperature 300 °C | 7.6 g/10 min @Load 11.0 lb, Temperature 572 °F | ASTM D1238 |
| 抗张强度(断裂) | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 | |
| 抗张强度(屈服) | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 | |
| 伸长率 (断裂) | 4.1 % | 4.1 % | Type I, 5 mm/min; ASTM D638 |
| 屈服伸长率 | 4.1 % | 4.1 % | Type I, 5 mm/min; ASTM D638 |
| 拉伸模量 | 7.58 GPa | 1100 ksi | 5 mm/min; ASTM D638 |
| 弯曲强度 | 135 MPa | 19600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 145 MPa | 21000 psi | 2 mm/min; ISO 178 | |
| 145 MPa | 21000 psi | 2 mm/min; ISO 178 | |
| 弯曲模量 | 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 7.15 GPa | 1040 ksi | 2 mm/min; ISO 178 | |
| 悬壁梁缺口冲击强度 | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| 悬壁梁无缺口冲击强度 | 2.67 J/cm | 5.00 ft-lb/in | ASTM D4812 |
| 悬壁梁缺口冲击强度 | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| 落锤总能量 | 9.00 J @Temperature 23.0 °C | 6.64 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| 表面电阻 | 10000 ohm | 10000 ohm | ASTM D257 |
| 线形热膨胀系数 - 流动 | 13.0 µm/m-°C @Temperature 23.0 - 150 °C | 7.22 µin/in-°F @Temperature 73.4 - 302 °F | ISO 11359-2 |
| 61.2 µm/m-°C @Temperature -30.0 - 30.0 °C | 34.0 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 | |
| 线性热膨胀系数,横向流动 | 57.0 µm/m-°C @Temperature 23.0 - 150 °C | 31.7 µin/in-°F @Temperature 73.4 - 302 °F | ISO 11359-2 |
| 158 µm/m-°C @Temperature -30.0 - 30.0 °C | 87.8 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C @Thickness 3.20 mm | 351 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| 181 °C @Thickness 6.40 mm | 358 °F @Thickness 0.252 in | unannealed; ASTM D648 | |
| 载荷下热变形温度(1.8 MPa) | 177 °C | 351 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 171 °C @Thickness 3.20 mm | 340 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 173 °C @Thickness 6.40 mm | 343 °F @Thickness 0.252 in | unannealed; ASTM D648 | |
| 维卡软化温度 | 180 °C | 356 °F | Rate B/50; ASTM D1525 |
| 180 °C | 356 °F | Rate B/120; ISO 306 | |
| UL RTI | 50.0 °C | 122 °F | UL 746B |
| UL RTI，机械冲击 | 50.0 °C | 122 °F | UL 746B |
| UL RTI，机械无冲击 | 50.0 °C | 122 °F | UL 746B |
| 可燃性(UL94) | V-1 @Thickness 1.49 mm | V-1 @Thickness 0.0587 in | UL 94 |
展开全文