可电镀PC/ABS 沙伯基础PC/ABS MC1300
CYCOLOY™ MC1300 resin
Polycarbonate + ABS
SABIC Innovative Plastics
产品说明：
CYCOLOY MC1300 resin is an injection moldable PC/ABS blend with excellent flow and impact performance. It is designed for plating applications mostly used in the automotive industry.
物性信息：
| 黄卡编号 | E121562-101286965 |
| 特性 | 抗撞击性，良好 可电镀 良好的流动性 |
| 用途 | 汽车领域的应用 |
| 加工方法 | 注射成型 |
| 多点数据 | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Elastic Modulus vs Temperature (ASTM D4065) Flexural DMA (ASTM D4065) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835) |
| 比重 | 1.10 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (260°C/5.0 kg) | 14 | g/10 min | ASTM D1238 |
| 收缩率 | 内部方法 | ||
| 流动 : 3.20 mm | 0.50 到 0.80 | % | 内部方法 |
| 横向流动 : 3.20 mm | 0.50 到 0.70 | % | 内部方法 |
| 吸水率 (24 hr) | 0.10 | % | ASTM D570 |
| 拉伸模量 1 | 2140 | MPa | ASTM D638 |
| 抗张强度 2 | ASTM D638 | ||
| 屈服 | 50.3 | MPa | ASTM D638 |
| 断裂 | 44.1 | MPa | ASTM D638 |
| 伸长率 3 | ASTM D638 | ||
| 屈服 | 8.6 | % | ASTM D638 |
| 断裂 | 150 | % | ASTM D638 |
| 弯曲模量 4(50.0 mm 跨距) | 2070 | MPa | ASTM D790 |
| 弯曲强度 5(屈服, 50.0 mm 跨距) | 72.4 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 | ASTM D256 | ||
| -30°C | 430 | J/m | ASTM D256 |
| 23°C | 530 | J/m | ASTM D256 |
| 装有测量仪表的落镖冲击 | ASTM D3763 | ||
| -30°C, Total Energy | 33.9 | J | ASTM D3763 |
| 23°C, Total Energy | 40.7 | J | ASTM D3763 |
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 3.20 mm | 116 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 3.20 mm | 98.9 | °C | ASTM D648 |
| 维卡软化温度 | 112 | °C | ASTM D1525 6 |
| 线形热膨胀系数 | ASTM E831 | ||
| 流动 : -40 到 40°C | 7.2E-5 | cm/cm/°C | ASTM E831 |
| 横向 : -40 到 40°C | 9.0E-5 | cm/cm/°C | ASTM E831 |
| 导热系数 | 0.20 | W/m/K | ASTM C177 |
| 干燥温度 | 98.9 到 104 | °C | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 干燥时间， | 8.0 | hr | |
| 建议的水分含量 | 0.040 | % | |
| 建议注射量 | 30 到 80 | % | |
| 料筒后部温度 | 249 到 282 | °C | |
| 料筒中部温度 | 254 到 288 | °C | |
| 料筒前部温度 | 254 到 288 | °C | |
| 射嘴温度 | 260 到 288 | °C | |
| 加工（熔体）温度 | 260 到 288 | °C | |
| 模具温度 | 76.7 到 98.9 | °C | |
| 背压 | 0.345 到 0.689 | MPa | |
| 螺杆转速 | 40 到 70 | rpm | |
| 排气孔深度 | 0.038 到 0.076 | mm |