出无卤阻燃原料 PC/PBT 沙伯基础 IQNH2900
沙伯基础 IQNH2900 产品说明：
UL94 V-0 Performance with Non-Brominated Flame Retardant. PCR% is up to 12% by using Valox iQ* resin.
物性信息：
| 比重 | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 26 g/10 min @Load 5.00 kg, Temperature 266 °C | 26 g/10 min @Load 11.0 lb, Temperature 511 °F | ASTM D1238 |
| 抗张强度(断裂) | 42.0 MPa | 6090 psi | Type I, 50 mm/min; ASTM D638 |
| 抗张强度(屈服) | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 |
| 伸长率 (断裂) | 65 % | 65 % | Type I, 50 mm/min; ASTM D638 |
| 屈服伸长率 | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D638 |
| 拉伸模量 | 2.48 GPa | 360 ksi | 50 mm/min; ASTM D638 |
| 弯曲强度 | 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 弯曲模量 | 2.24 GPa | 325 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 悬壁梁缺口冲击强度 | 5.50 J/cm | 10.3 ft-lb/in | ASTM D256 |
| 落锤总能量 | 65.0 J @Temperature 23.0 °C | 47.9 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| 载荷下热变形温度(1.8 MPa) | 77.0 °C @Thickness 3.20 mm | 171 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| 维卡软化温度 | 100 °C | 212 °F | Rate B/50; ASTM D1525 |
| 可燃性(UL94) | V-1 @Thickness 1.10 mm | V-1 @Thickness 0.0433 in | UL 94 |
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL 94 | |
| 5VB @Thickness 2.50 mm | 5VB @Thickness 0.0984 in | UL 94 |
展开全文