PC 德国科思创（拜耳）8025 20%带压花的玻纤 挤出 注射成型
Makrolon® 8025
黄卡编号
屈服, 23°C58.0MPaISO 527-2/50 断裂, 23°C50.0MPaISO 527-2/5拉伸应变
屈服, 23°C3.5%ISO 527-2/50 断裂, 23°C6.5%ISO 527-2/5拉伸蠕变模量
ISO 899-1 1 hr3700MPaISO 899-1 1000 hr3500MPaISO 899-1弯曲模量 4(23°C)3700MPaISO 178弯曲应力 5
ISO 178 3.5% 应变, 23°C95.0MPaISO 178 23°C100MPaISO 178Flexural Strain at Flexural Strength (23°C) 65.4%ISO 178可燃性额定值单位制测试方法Application of Flame from Small Burner - Method K and F (2.00 mm)K1, F1
DIN 53438-1, -3Burning Rate - US-FMVSS (> 1.00 mm)passed
ISO 3795Flash Ignition Temperature470°CASTM D1929Needle Flame Test
IEC 60695-11-5 Method F : 1.50 mm2.0minIEC 60695-11-5 Method F : 2.00 mm2.0minIEC 60695-11-5 Method F : 3.00 mm2.0minIEC 60695-11-5 Method K : 1.50 mm1.0minIEC 60695-11-5 Method K : 2.00 mm1.0minIEC 60695-11-5 Method K : 3.00 mm2.0minIEC 60695-11-5Self Ignition Temperature550°CASTM D1929补充信息额定值
测试方法Electrolytical Corrosion (23°C)A1
IEC 60426ISO ShortnameISO 7391-PC,GR,(,,)-05-5,GF20
冲击性能额定值单位制测试方法简支梁缺口冲击强度 7(23°C, 完全断裂)12kJ/m²ISO 7391简支梁无缺口冲击强度
ISO 179/1eU -60°C, 完全断裂65kJ/m²ISO 179/1eU -30°C, 完全断裂65kJ/m²ISO 179/1eU 23°C, 完全断裂55kJ/m²ISO 179/1eU悬壁梁缺口冲击强度 8(23°C, 完全断裂)12kJ/m²ISO 7391多轴向仪器化冲击能量
ISO 6603-2 -30°C10.0JISO 6603-2 23°C20.0JISO 6603-2多轴向仪器化冲击力峰值
ISO 6603-2 -30°C2800NISO 6603-2 23°C3300NISO 6603-2热性能额定值单位制测试方法热变形温度
0.45 MPa, 未退火141°CISO 75-2/B 1.8 MPa, 未退火134°CISO 75-2/A维卡软化温度
--146°CISO 306/B50 --147°CISO 306/B120Ball Pressure Test (137°C)Pass
IEC 60695-10-2线形热膨胀系数
ISO 11359-2 流动 : 23 到 55°C4.5E-5cm/cm/°CISO 11359-2 横向 : 23 到 55°C5.5E-5cm/cm/°CISO 11359-2导热系数 9(23°C)0.23W/m/KISO 8302RTI Elec (1.50 mm)125°CUL 746RTI Imp (1.50 mm)115°CUL 746RTI (1.50 mm)125°CUL 746电气性能额定值单位制测试方法表面电阻率1.0E+16ohmsIEC 60093体积电阻率 (23°C)1.0E+16ohms·cmIEC 60093介电强度 (23°C, 1.00 mm)36kV/mmIEC 60243-1相对电容率
IEC 60250 23°C, 100 Hz3.30
IEC 60250 23°C, 1 MHz3.30
IEC 60250耗散因数
IEC 60250 23°C, 100 Hz1.0E-3
IEC 60250 23°C, 1 MHz9.0E-3
IEC 60250漏电起痕指数
IEC 60112 解决方案 A175VIEC 60112 解决方案 B125VIEC 60112可燃性额定值单位制测试方法UL 阻燃等级
UL 94 1.50 mmV-2
UL 94 6.00 mmV-1
UL 94灼热丝易燃指数
IEC 60695-2-12 0.750 mm800°CIEC 60695-2-12 1.50 mm960°CIEC 60695-2-12 2.00 mm960°CIEC 60695-2-12 3.00 mm960°CIEC 60695-2-12 4.00 mm960°CIEC 60695-2-12热灯丝点火温度
IEC 60695-2-13 0.750 mm850°CIEC 60695-2-13 2.00 mm875°CIEC 60695-2-13 3.00 mm875°CIEC 60695-2-13极限氧指数 1032%ISO 4589-2
20% 带压花的玻璃纤维
物性信息：
黄卡编号
E41613-233157
填料/增强材料带压花的玻璃纤维, 20% 填料按重量
特性脱模性能良好
粘度，高
RoHS 合规性RoHS 合规
外观不透明
可用颜色
加工方法挤出
注射成型
物理性能额定值单位制测试方法密度 (23°C)1.34g/cm³ISO 1183表观密度 10.69g/cm³ISO 60熔流率（熔体流动速率） (300°C/1.2 kg)6.5g/10 minISO 1133溶化体积流率（MVR） (300°C/1.2 kg)6.00cm³/10minISO 1133收缩率
垂直流动方向0.30 到 0.45%ISO 2577 流动方向0.30 到 0.45%ISO 2577 垂直流动方向 : 2.00 mm 20.35%ISO 294-4 流动方向 : 2.00 mm 30.55%ISO 294-4吸水率
ISO 62 饱和, 23°C0.24%ISO 62 平衡, 23°C, 50% RH0.10%ISO 62
屈服, 23°C58.0MPaISO 527-2/50 断裂, 23°C50.0MPaISO 527-2/5拉伸应变
屈服, 23°C3.5%ISO 527-2/50 断裂, 23°C6.5%ISO 527-2/5拉伸蠕变模量
ISO 899-1 1 hr3700MPaISO 899-1 1000 hr3500MPaISO 899-1弯曲模量 4(23°C)3700MPaISO 178弯曲应力 5
ISO 178 3.5% 应变, 23°C95.0MPaISO 178 23°C100MPaISO 178Flexural Strain at Flexural Strength (23°C) 65.4%ISO 178可燃性额定值单位制测试方法Application of Flame from Small Burner - Method K and F (2.00 mm)K1, F1
DIN 53438-1, -3Burning Rate - US-FMVSS (> 1.00 mm)passed
ISO 3795Flash Ignition Temperature470°CASTM D1929Needle Flame Test
IEC 60695-11-5 Method F : 1.50 mm2.0minIEC 60695-11-5 Method F : 2.00 mm2.0minIEC 60695-11-5 Method F : 3.00 mm2.0minIEC 60695-11-5 Method K : 1.50 mm1.0minIEC 60695-11-5 Method K : 2.00 mm1.0minIEC 60695-11-5 Method K : 3.00 mm2.0minIEC 60695-11-5Self Ignition Temperature550°CASTM D1929补充信息额定值
测试方法Electrolytical Corrosion (23°C)A1
IEC 60426ISO ShortnameISO 7391-PC,GR,(,,)-05-5,GF20
冲击性能额定值单位制测试方法简支梁缺口冲击强度 7(23°C, 完全断裂)12kJ/m²ISO 7391简支梁无缺口冲击强度
ISO 179/1eU -60°C, 完全断裂65kJ/m²ISO 179/1eU -30°C, 完全断裂65kJ/m²ISO 179/1eU 23°C, 完全断裂55kJ/m²ISO 179/1eU悬壁梁缺口冲击强度 8(23°C, 完全断裂)12kJ/m²ISO 7391多轴向仪器化冲击能量
ISO 6603-2 -30°C10.0JISO 6603-2 23°C20.0JISO 6603-2多轴向仪器化冲击力峰值
ISO 6603-2 -30°C2800NISO 6603-2 23°C3300NISO 6603-2热性能额定值单位制测试方法热变形温度
0.45 MPa, 未退火141°CISO 75-2/B 1.8 MPa, 未退火134°CISO 75-2/A维卡软化温度
--146°CISO 306/B50 --147°CISO 306/B120Ball Pressure Test (137°C)Pass
IEC 60695-10-2线形热膨胀系数
ISO 11359-2 流动 : 23 到 55°C4.5E-5cm/cm/°CISO 11359-2 横向 : 23 到 55°C5.5E-5cm/cm/°CISO 11359-2导热系数 9(23°C)0.23W/m/KISO 8302RTI Elec (1.50 mm)125°CUL 746RTI Imp (1.50 mm)115°CUL 746RTI (1.50 mm)125°CUL 746电气性能额定值单位制测试方法表面电阻率1.0E+16ohmsIEC 60093体积电阻率 (23°C)1.0E+16ohms·cmIEC 60093介电强度 (23°C, 1.00 mm)36kV/mmIEC 60243-1相对电容率
IEC 60250 23°C, 100 Hz3.30
IEC 60250 23°C, 1 MHz3.30
IEC 60250耗散因数
IEC 60250 23°C, 100 Hz1.0E-3
IEC 60250 23°C, 1 MHz9.0E-3
IEC 60250漏电起痕指数
IEC 60112 解决方案 A175VIEC 60112 解决方案 B125VIEC 60112可燃性额定值单位制测试方法UL 阻燃等级
UL 94 1.50 mmV-2
UL 94 6.00 mmV-1
UL 94灼热丝易燃指数
IEC 60695-2-12 0.750 mm800°CIEC 60695-2-12 1.50 mm960°CIEC 60695-2-12 2.00 mm960°CIEC 60695-2-12 3.00 mm960°CIEC 60695-2-12 4.00 mm960°CIEC 60695-2-12热灯丝点火温度
IEC 60695-2-13 0.750 mm850°CIEC 60695-2-13 2.00 mm875°CIEC 60695-2-13 3.00 mm875°CIEC 60695-2-13极限氧指数 1032%ISO 4589-2