Vydyne® R533H聚酰胺6633% 玻璃纤维增强材料Ascend Performance Materials Operations LLC产品说明：

Vydyne R533H is 33% glass-fiber reinforced, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is lubricated for improved machine feed and flow.

Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.

Vydyne R533H resin is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also, Vydyne R533H resin has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions.

Typical Applications/End Uses:
Vydyne R533H resin has been used for many under-the-hood automotive applications, motor housings for power tools and garden appliances. This resin has also been used in miscellaneous brackets, gears and clips that require high rigidity and strength.

添加剂	热稳定剂 润滑剂
特性	刚性，高 高强度 流动性高 热稳定性 润滑 脱模性能良好
用途	齿轮 动力/其它工具 汽车的发动机罩下的零件 外壳
机构评级	ASTM D 4066 PA0121G35 ASTM D 6779 PA0121G35
UL文件号	E70062
外观	自然色
形式	粒子
加工方法	注射成型

物理性能干燥调节后的单位制测试方法

密度	1.40	--	g/cm³	ISO 1183
收缩率				ISO 294-4
垂直流动方向 : 23°C, 2.00 mm	0.90	--	%	ISO 294-4
流动方向 : 23°C, 2.00 mm	0.40	--	%	ISO 294-4
吸水率				ISO 62
23°C, 24 hr	0.80	--	%	ISO 62
平衡, 23°C, 50% RH	1.7	--	%	ISO 62

机械性能干燥调节后的单位制测试方法

拉伸模量 (23°C)	10600	7900	MPa	ISO 527-2
拉伸应力 (断裂, 23°C)	205	145	MPa	ISO 527-2
拉伸应变 (断裂, 23°C)	3.0	5.0	%	ISO 527-2
弯曲模量 (23°C)	10200	6500	MPa	ISO 178
弯曲应力 (23°C)	290	200	MPa	ISO 178
泊松比	0.40	--		ISO 527-2