PA66德国巴斯夫A3EG5 玻纤25%
25% 玻璃纤维增强材料
BASF CorporationUltramid® A3EG5聚酰胺66产品说明：
Glass fibre reinforced injection moulding grade for machinery components and housings of high stiffness and dimensional stability such as coil formers and bearing cages. Also used for electrically insulating parts.
| 特性 | 尺寸稳定性良好 刚性，高 耐油性能 |
| 用途 | 电子绝缘 机器/机械部件 外壳 |
| 机构评级 | EC 1907/2006 (REACH) |
| RoHS 合规性 | RoHS 合规 |
| 形式 | 粒子 |
| 加工方法 | 注射成型 |
| 多点数据 | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2) |
| 密度 | 1.32 | -- | g/cm³ | ISO 1183 |
| 表观密度 | 0.70 | -- | g/cm³ | |
| 溶化体积流率（MVR） (275°C/5.0 kg) | 50.0 | -- | cm³/10min | ISO 1133 |
| 收缩率 | ISO 294-4 | |||
| 垂直流动方向 | 1.1 | -- | % | ISO 294-4 |
| 流动方向 | 0.48 | -- | % | ISO 294-4 |
| 吸水率 | ISO 62 | |||
| 饱和, 23°C | 5.7 到 6.3 | -- | % | ISO 62 |
| 平衡, 23°C, 50% RH | 1.7 到 2.1 | -- | % | ISO 62 |
| 粘数 (96% H2SO4) | 145 | -- | cm³/g | ISO 307 |
| 模具收缩性 - constrained 1 | 0.55 | -- | % |
| 温度指数 - at 50% loss of tensile strength | IEC 60216 | |||
| -- 2 | 135 | -- | °C | IEC 60216 |
| -- 3 | 165 | -- | °C | IEC 60216 |
| 使用温度 - short cycle operation | 240 | -- | °C |
| Automotive Materials (> 1.00 mm) | Passed | -- | FMVSS 302 | |
| Polymer Abbreviation | PA66-GF25 | -- |
| Screw Speed | mm/sec |
| 拉伸模量 | 8600 | 6500 | MPa | ISO 527-2 |
| 拉伸应力 (断裂) | 175 | 120 | MPa | ISO 527-2 |
| 拉伸应变 (断裂) | 3.0 | 6.0 | % | ISO 527-2 |
| 拉伸蠕变模量 4(1000 hr) | -- | 4300 | MPa | ISO 899-1 |
| 弯曲模量 | 7600 | 6000 | MPa | ISO 178 |
| 弯曲应力 | 260 | 200 | MPa | ISO 178 |
| 简支梁缺口冲击强度 | ISO 179/1eA | |||
| -30°C | 9.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 12 | 18 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 | ISO 179/1eU | |||
| -30°C | 55 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 65 | 90 | kJ/m² | ISO 179/1eU |
| 悬壁梁缺口冲击强度 (23°C) | 9.5 | 15 | kJ/m² | ISO 180/A |