Texin® 260 物性表

基本信息
特性

抗撞击性，良好

良好的柔韧性

良好耐磨损性

耐燃油性

耐油性能

韧性良好

用途

车轮

垫圈

密封件

机构评级

FDA 21 CFR 177.1680

FDA 21 CFR 177.2600

外观

自然色

加工方法

注射成型

物理性能额定值单位制测试方法比重1.22g/cm³ASTM D792, ISO 1183收缩率


    流动 : 2.54 mm0.80%ASTM D955    横向流动 : 2.54 mm0.80%ASTM D955    垂直流动方向 : 2.54 mm0.80%ISO 2577    流动方向 : 2.54 mm0.80%ISO 2577硬度额定值单位制测试方法肖氏硬度 (邵氏 D)60
ASTM D2240, ISO 868机械性能额定值单位制测试方法弯曲模量 (23°C)296MPaASTM D790泰伯耐磨性


    1000 Cycles, 1000 g, H-18 转轮50.0mgISO 4649    1000 Cycles, 1000 g, H-18 转轮50.0mgASTM D1044弹性体额定值单位制测试方法拉伸应力


    50%应变20.0MPaISO 37, ASTM D412 应变22.1MPaASTM D412, ISO 37    300%应变40.0MPaASTM D412, ISO 37抗张强度 (屈服)60.0MPaASTM D412, ISO 37伸长率 (断裂)420%ASTM D412, ISO 37撕裂强度


    -- 1175kN/mASTM D624    --180kN/mISO 34-1压缩变形

ASTM D395B    23°C, 22 hr 221%ASTM D395B    23°C, 22 hr27%ASTM D395B    70°C, 22 hr 335%ASTM D395B    70°C, 22 hr55%ASTM D395B巴肖氏弹性35%ASTM D2632老化额定值单位制测试方法空气中拉伸强度的变化率


    100°C, 70 hr7.0%ASTM D573, ISO 216     应变, 100°C, 70 hr13%ASTM D573    300% 应变, 100°C, 70 hr8.0%ASTM D573    100°C, 168 hr1.0%ASTM D573, ISO 216     应变, 100°C, 168 hr-1.0%ASTM D573    300% 应变, 100°C, 168 hr-1.0%ASTM D573    100°C, 336 hr9.0%ASTM D573, ISO 216     应变, 100°C, 336 hr23%ASTM D573    300% 应变, 100°C, 336 hr-3.0%ASTM D573    100°C, 504 hr13%ASTM D573, ISO 216     应变, 100°C, 504 hr5.0%ASTM D573    300% 应变, 100°C, 504 hr-4.0%ASTM D573    125°C, 70 hr16%ASTM D573, ISO 216     应变, 125°C, 70 hr-2.0%ASTM D573    300% 应变, 125°C, 70 hr-18%ASTM D573    125°C, 168 hr21%ASTM D573, ISO 216     应变, 125°C, 168 hr8.0%ASTM D573    300% 应变, 125°C, 168 hr-12%ASTM D573    125°C, 336 hr6.0%ASTM D573, ISO 216     应变, 125°C, 336 hr-7.0%ASTM D573    300% 应变, 125°C, 336 hr-24%ASTM D573    125°C, 504 hr-2.0%ASTM D573, ISO 216    300% 应变 125°C, 504 hr-26%ISO 216空气中极限伸长率的变化率

ASTM D573, ISO 216    100°C, 70 hr1.0%ASTM D573, ISO 216    100°C, 168 hr8.0%ASTM D573, ISO 216    100°C, 336 hr17%ASTM D573, ISO 216    100°C, 504 hr24%ASTM D573, ISO 216    125°C, 70 hr51%ASTM D573, ISO 216    125°C, 168 hr51%ASTM D573, ISO 216    125°C, 336 hr52%ASTM D573, ISO 216    125°C, 504 hr44%ASTM D573, ISO 216空气中硬度计硬度的变化率

ASTM D573, ISO 216    支撐 D, 100°C, 70 hr0.0
ASTM D573, ISO 216    支撐 D, 100°C, 168 hr-2.0
ASTM D573, ISO 216    支撐 D, 100°C, 336 hr-3.0
ASTM D573, ISO 216    支撐 D, 100°C, 504 hr-3.0
ASTM D573, ISO 216    支撐 D, 125°C, 70 hr-2.0
ASTM D573, ISO 216    支撐 D, 125°C, 168 hr-3.0
ASTM D573, ISO 216    支撐 D, 125°C, 336 hr-4.0
ASTM D573, ISO 216    支撐 D, 125°C, 504 hr-3.0
ASTM D573, ISO 216