SABIC Innovative Plastics Cycoloy® CX5430 PC+ABS 物性表
| 比重 | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| 密度 | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 | |
| 水分吸收 | 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.30 % | 0.30 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 19 g/10 min @Load 5.00 kg, Temperature 260 °C | 19 g/10 min @Load 11.0 lb, Temperature 500 °F | ASTM D1238 |
| 化合物熔体指数 | 18 g/10 min @Load 5.00 kg, Temperature 260 °C | 18 g/10 min @Load 11.0 lb, Temperature 500 °F | MVR [cm^3/10 min]; ISO 1133 |
| Hardness, Rockwell L | 90 | 90 | ISO 2039-2 |
| 洛氏硬度（R 级） | 115 | 115 | ISO 2039-2 |
| 抗张强度(断裂) | 44.0 MPa | 6380 psi | 5 mm/min; ISO 527 |
| 44.0 MPa | 6380 psi | 50 mm/min; ISO 527 | |
| 45.0 MPa | 6530 psi | Type I, 50 mm/min; ASTM D638 | |
| 抗张强度(屈服) | 44.0 MPa | 6380 psi | 5 mm/min; ISO 527 |
| 48.0 MPa | 6960 psi | 50 mm/min; ISO 527 | |
| 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 | |
| 伸长率 (断裂) | >= 50 % | >= 50 % | Type I, 50 mm/min; ASTM D638 |
| >= 50 % | >= 50 % | 5 mm/min; ISO 527 | |
| >= 50 % | >= 50 % | 50 mm/min; ISO 527 | |
| 屈服伸长率 | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| 5.0 % | 5.0 % | 5 mm/min; ISO 527 | |
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |
| 拉伸模量 | 2.40 GPa | 348 ksi | 5 mm/min; ASTM D638 |
| 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 | |
| 弯曲强度 | 75.0 MPa | 10900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 75.0 MPa | 10900 psi | 2 mm/min; ISO 178 | |
| 弯曲模量 | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 | |
| 悬壁梁缺口冲击强度 | 1.10 J/cm | 2.06 ft-lb/in | Izod Impact, double-gated, 23°C; SABIC Method |
| 5.00 J/cm | 9.37 ft-lb/in | ASTM D256 | |
| 2.50 J/cm @Temperature -30.0 °C | 4.68 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*3; ISO 180/1A | |
| 20.0 kJ/m² @Temperature -30.0 °C | 9.52 ft-lb/in² @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
| 简支梁缺口冲击强度 | 4.00 J/cm² | 19.0 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 2.00 J/cm² @Temperature -30.0 °C | Edgew 80*10*3 sp=62mm; ISO 179/1eA | ||
| Dart Drop, Total Energy | 40.0 J @Temperature -30.0 °C | 29.5 ft-lb @Temperature -22.0 °F | ASTM D3763 |
| 55.0 J @Temperature 23.0 °C | 40.6 ft-lb @Temperature 73.4 °F | ASTM D3763 | |
| 冲击试验 | 80.0 J | 59.0 ft-lb | Multiaxial Impact; ISO 6603 |
| 泰伯磨损，毫克/1000次 | 70 | 70 | CS-17, 1 kg; SABIC Method |
| 体积电阻率 | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D257 |
| 表面电阻 | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ASTM D257 |
| 介电常数 | 2.7 @Frequency 1000 Hz | 2.7 @Frequency 1000 Hz | IEC 60250 |
| 2.9 @Frequency 50.0 - 60.0 Hz | 2.9 @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
| 介电强度 | 25.0 kV/mm @Thickness 1.50 mm | 635 kV/in @Thickness 0.0591 in | in oil; IEC 60243-1 |
| 35.0 kV/mm @Thickness 0.800 mm | 889 kV/in @Thickness 0.0315 in | in oil; IEC 60243-1 | |
| 耗散因数 | 0.010 @Frequency 50.0 - 60.0 Hz | 0.010 @Frequency 50.0 - 60.0 Hz | IEC 60250 |
| 0.011 @Frequency 1.00e+6 Hz | 0.011 @Frequency 1.00e+6 Hz | IEC 60250 |
| 线形热膨胀系数 - 流动 | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 44.4 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C | ISO 11359-2 | ||
| 线性热膨胀系数,横向流动 | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C | ISO 11359-2 | |
| 导热系数 | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C177 |
| 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ISO 8302 | |
| Hot Ball Pressure Test | <= 100 °C | <= 212 °F | IEC 60695-10-2 |
| 载荷下热变形温度(0.46 MPa) | 117 °C | 243 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 115 °C @Thickness 3.20 mm | 239 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 载荷下热变形温度(1.8 MPa) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 95.0 °C @Thickness 3.20 mm | 203 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 维卡软化温度 | 114 °C | 237 °F | Rate B/50; ISO 306 |
| 115 °C | 239 °F | Rate B/120; ISO 306 | |
| 115 °C | 239 °F | Rate B/50; ASTM D1525 | |
| UL RTI | 60.0 °C | 140 °F | UL 746B |
| UL RTI，机械冲击 | 60.0 °C | 140 °F | UL 746B |
| UL RTI，机械无冲击 | 60.0 °C | 140 °F | UL 746B |
| 可燃性(UL94) | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL 94 |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | UL 94 | |
| 灼热丝试验 | 650 °C @Thickness 3.20 mm | 1200 °F @Thickness 0.126 in | IEC 60695-2-12 |