沙伯基础PC/ABS CY4000M 7M1D166
沙伯基础PC/ABS CY4000M 7M1D166物性信息：
| 比重 | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| 水分吸收 | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.60 % | 0.60 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 25 g/10 min @Load 2.16 kg, Temperature 260 °C | 25 g/10 min @Load 4.76 lb, Temperature 500 °F | ASTM D1238 |
| 抗张强度(断裂) | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 |
| 抗张强度(屈服) | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 |
| 伸长率 (断裂) | 44 % | 44 % | Type I, 50 mm/min; ASTM D638 |
| 屈服伸长率 | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D638 |
| 弯曲强度 | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 弯曲模量 | 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 悬壁梁缺口冲击强度 | 5.50 J/cm | 10.3 ft-lb/in | ASTM D256 |
| 1.20 J/cm @Temperature -30.0 °C | 2.25 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 落锤总能量 | 55.0 J @Temperature 23.0 °C | 40.6 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| 线形热膨胀系数 - 流动 | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 44.4 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 线性热膨胀系数,横向流动 | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 44.4 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 载荷下热变形温度(1.8 MPa) | 80.0 °C @Thickness 3.20 mm | 176 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| 维卡软化温度 | 98.0 °C | 208 °F | Rate B/50; ASTM D1525 |
| 98.0 °C | 208 °F | Rate B/50; ISO 306 | |
| 100 °C | 212 °F | Rate B/120; ISO 306 | |
| 可燃性(UL94) | V-0 @Thickness 2.50 mm | V-0 @Thickness 0.0984 in | UL 94 by SABIC-IP |