TPU 2363-80A美国Lubrizol
Lubrizol Pellethane® 2363-80A Thermoplastic Polyurethane Elastomer 物性表
| 密度 | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| 线性成型收缩率,Flow | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| 线性成型收缩率，横向 | 0.00 - 0.0040 cm/cm | 0.00 - 0.0040 in/in | ASTM D955 |
| 熔体流动速率 | 23 g/10 min @Load 1.20 kg, Temperature 224 °C | 23 g/10 min @Load 2.65 lb, Temperature 435 °F | ASTM D1238 |
| 肖氏硬度 (邵氏 A) | 81 | 81 | ASTM D2240 |
| 极限抗拉强度 | 35.8 MPa | 5190 psi | ASTM D412 |
| 伸长率 (断裂) | 550 % | 550 % | ASTM D412 |
| 50% Modulus | 0.00410 GPa | 0.595 ksi | ASTM D412 |
| 模量 | 0.00610 GPa | 0.885 ksi | ASTM D412 |
| 300％模量 | 0.0121 GPa | 1.75 ksi | ASTM D412 |
| 撕裂强度 | 82.3 kN/m | 470 pli | Die C; ASTM D624 |
| 泰伯磨损，毫克/1000次 | 20 | 20 | H22 Wheel, 1000g; ASTM D1044 |
| 压缩变形 | 25 % @Temperature 25.0 °C, Time 79200 sec | 25 % @Temperature 77.0 °F, Time 22.0 hour | ASTM D395 Method B |
| 30 % @Temperature 70.0 °C, Time 79200 sec | 30 % @Temperature 158 °F, Time 22.0 hour | ASTM D395 Method B | |
| Tensile Set | 30 % | 30 % | Elongation set after break; ASTM D412 |
| 线性热膨胀系数 | 170 µm/m-°C @Temperature -80.0 - -30.0 °C | 94.4 µin/in-°F @Temperature -112 - -22.0 °F | ASTM D696 |