美国路博润2363-90A 物性表
密度 | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
线性成型收缩率,Flow | 0.0050 - 0.0060 cm/cm | 0.0050 - 0.0060 in/in | ASTM D955 |
线性成型收缩率,横向 | 0.0050 - 0.0060 cm/cm | 0.0050 - 0.0060 in/in | ASTM D955 |
熔体流动速率 | 30 g/10 min @Load 1.20 kg, Temperature 224 °C | 30 g/10 min @Load 2.65 lb, Temperature 435 °F | ASTM D1238 |
肖氏硬度 (邵氏 A) | 90 | 90 | ASTM D2240 |
极限抗拉强度 | 40.3 MPa | 5850 psi | ASTM D412 |
伸长率 (断裂) | 500 % | 500 % | ASTM D412 |
50% Modulus | 0.00830 GPa | 1.20 ksi | ASTM D412 |
模量 | 0.0117 GPa | 1.70 ksi | ASTM D412 |
300%模量 | 0.0207 GPa | 3.00 ksi | ASTM D412 |
弯曲模量 | 0.0758 GPa | 11.0 ksi | ASTM D790 |
撕裂强度 | 100 kN/m | 571 pli | Die C; ASTM D624 |
泰伯磨损,毫克/1000次 | 10 | 10 | H22 Wheel, 1000g; ASTM D1044 |
压缩变形 | 25 % @Temperature 25.0 °C, Time 79200 sec | 25 % @Temperature 77.0 °F, Time 22.0 hour | ASTM D395, Method B |
30 % @Temperature 70.0 °C, Time 79200 sec | 30 % @Temperature 158 °F, Time 22.0 hour | ASTM D395, Method B | |
Tensile Set | 30 % | 30 % | Elongation set after break; ASTM D412 |