40%玻纤 PPO GFN1740V-73701 基础创新塑料(美国)
产品说明:Noryl* GFN1740V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; this grade has been developed for fluid engineering applications where higher static stiffness is required. Noryl* GFN1740V has been certified for potable water applications up to 85C in Europe and North America in limited colours
SABIC Innovative Plastics NORYL GFN1740V PPE+PS 物性表
| 比重 | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| 密度 | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| 水分吸收 | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.20 % | 0.20 % | ISO 62 |
| 线性成型收缩率,Flow | 0.00090 - 0.0015 cm/cm @Thickness 3.20 mm | 0.00090 - 0.0015 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 10 g/10 min @Load 5.00 kg, Temperature 300 °C | 10 g/10 min @Load 11.0 lb, Temperature 572 °F | ASTM D1238 |
| 化合物熔体指数 | 20 g/10 min @Load 10.0 kg, Temperature 300 °C | 20 g/10 min @Load 22.0 lb, Temperature 572 °F | MVR [cm^3/10 min]; ISO 1133 |
| 抗张强度(断裂) | 155 MPa | 22500 psi | 5 mm/min; ISO 527 |
| 165 MPa | 23900 psi | Type I, 5 mm/min; ASTM D638 | |
| 抗张强度(屈服) | 155 MPa | 22500 psi | 5 mm/min; ISO 527 |
| 165 MPa | 23900 psi | Type I, 5 mm/min; ASTM D638 | |
| 伸长率 (断裂) | 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 |
| 1.8 % | 1.8 % | 5 mm/min; ISO 527 | |
| 屈服伸长率 | 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 |
| 1.8 % | 1.8 % | 5 mm/min; ISO 527 | |
| 拉伸模量 | 11.3 GPa | 1640 ksi | 1 mm/min; ISO 527 |
| 13.8 GPa | 2000 ksi | 5 mm/min; ASTM D638 | |
| 弯曲强度 | 195 MPa | 28300 psi | 2 mm/min; ISO 178 |
| 225 MPa | 32600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | 9.50 GPa | 1380 ksi | 2 mm/min; ISO 178 |
| 11.7 GPa | 1700 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 悬壁梁缺口冲击强度 | 1.08 J/cm | 2.02 ft-lb/in | ASTM D256 |
| 0.900 J/cm @Temperature -30.0 °C | 1.69 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 悬壁梁无缺口冲击强度 | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| 30.0 kJ/m² @Temperature -30.0 °C | 14.3 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |
| 简支梁无缺口冲击强度 | 3.00 J/cm² | 14.3 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 落锤总能量 | 18.0 J @Temperature 23.0 °C | 13.3 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| 线形热膨胀系数 - 流动 | 20.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 11.1 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 20.0 µm/m-°C @Temperature -40.0 - 40.0 °C | ISO 11359-2 | ||
| 线性热膨胀系数,横向流动 | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 38.9 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C | ISO 11359-2 | ||
| 载荷下热变形温度(1.8 MPa) | 147 °C | 297 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 148 °C @Thickness 3.20 mm | 298 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 维卡软化温度 | 151 °C | 304 °F | Rate B/50; ASTM D1525 |
| 152 °C | 306 °F | Rate B/50; ISO 306 | |
| 161 °C | 322 °F | Rate B/120; ISO 306 |