17%矿物 PPO HS2000X 沙伯基础(美国)

NORYL™ HS2000X resin聚苯醚 + PS17% 矿物填料SABIC Innovative Plastics产品说明：

PPE+PS blend. 17% Mineral reinforced. Non-brominated, non-chlorinated FR system. UL94 V0 and 5VA listing. UL746C f1. Radiant panel listing. Dielectric strength. Dimensional stability. Suitable for E/E market indoor/outdoor applications including electrical ceiling boxes and smoke detectors.

NORYL™ HS2000X resin 物性表

基本信息
黄卡编号

E121562-221170

填料/增强材料

矿物填料, 17% 填料按重量

添加剂

阻燃性

特性

Chlorine Free

尺寸稳定性良好

无溴

阻燃性

用途

电气/电子应用领域

室外应用

加工方法

注射成型

多点数据

Compressive Stress vs. Strain (ASTM D695)

Elastic Modulus vs Temperature (ASTM D4065)

Flexural DMA (ASTM D4065)

Instrumented Impact (Energy) (ASTM D3763)

Instrumented Impact (Load) (ASTM D3763)

Tensile Creep (ASTM D2990)

Tensile Fatigue

Tensile Stress vs. Strain (ASTM D638)

Thermal Conductivity vs. Temperature (ASTM E1530)

物理性能额定值单位制测试方法比重1.25g/cm³ASTM D792熔流率（熔体流动速率）

ASTM D1238    280°C/5.0 kg7.6g/10 minASTM D1238    300°C/5.0 kg7.6g/10 minASTM D1238溶化体积流率（MVR）

ISO 1133    280°C/5.0 kg6.80cm³/10minISO 1133    300°C/5.0 kg6.80cm³/10minISO 1133收缩率 - 流动 (3.20 mm)0.50 到 0.70%内部方法室外适用性f1
UL 746C机械性能额定值单位制测试方法拉伸模量


    -- 13650MPaASTM D638    --4000MPaISO 527-2/1抗张强度


    屈服 274.0MPaASTM D638    屈服71.7MPaISO 527-2    断裂 360.0MPaASTM D638    断裂57.1MPaISO 527-2伸长率


    屈服3.8%ASTM D638    屈服3.7%ISO 527-2    断裂 48.4%ASTM D638    断裂11%ISO 527-2弯曲模量


    100 mm 跨距 53550MPaASTM D790    50.0 mm 跨距 63670MPaASTM D790    --3800MPaISO 178弯曲应力


    --117MPaISO 178    屈服, 100 mm 跨距 7117MPaASTM D790    断裂, 50.0 mm 跨距 8117MPaASTM D790冲击性能额定值单位制测试方法简支梁缺口冲击强度 (23°C)10kJ/m²ISO 179/2C悬壁梁缺口冲击强度


    23°C130J/mASTM D256    23°C 99.7kJ/m²ISO 180/1A无缺口悬臂梁冲击 (23°C)2200J/mASTM D4812反向缺口冲击 (3.20 mm)810J/mASTM D256装有测量仪表的落镖冲击 (23°C, Total Energy)443JASTM D3763热性能额定值单位制测试方法载荷下热变形温度


    0.45 MPa, 未退火, 3.20 mm117°CASTM D648    0.45 MPa, 未退火, 6.40 mm128°CASTM D648    0.45 MPa, 未退火, 100 mm 跨距 10126°CISO 75-2/Be    1.8 MPa, 未退火, 3.20 mm108°CASTM D648    1.8 MPa, 未退火, 6.40 mm116°CASTM D648    1.8 MPa, 未退火, 100 mm 跨距 11111°CISO 75-2/Ae维卡软化温度


    --132°CISO 306/B50    --136°CISO 306/B120线形热膨胀系数

ASTM E831    流动 : -40 到 40°C7.1E-5cm/cm/°CASTM E831    横向 : -40 到 40°C7.8E-5cm/cm/°CASTM E831RTI Elec100°CUL 746RTI Imp85.0°CUL 746RTI100°CUL 746电气性能额定值单位制测试方法表面电阻率> 1.0E+16ohmsASTM D257体积电阻率1.2E+16ohms·cmASTM D257介电强度 (3.20 mm, in Oil)17kV/mmASTM D149介电常数

ASTM D150    50 Hz2.89
ASTM D150    60 Hz2.89
ASTM D150    1 MHz2.70
ASTM D150耗散因数

ASTM D150    50 Hz0.017
ASTM D150    60 Hz0.017
ASTM D150    1 MHz4.4E-3
ASTM D150耐电弧性 12PLC 6
ASTM D495相比耐漏电起痕指数(CTI)PLC 2
UL 746高电弧燃烧指数(HAI)PLC 2
UL 746高电压电弧起痕速率 (HVTR)PLC 3
UL 746热丝引燃 (HWI)PLC 0
UL 746可燃性额定值单位制测试方法UL 阻燃等级

UL 94    1.47 mmV-0
UL 94    2.01 mm5VA
UL 94Radiant Panel Listing (UL)YES