PPO 沙伯基础(美国) N190HX-701
SABIC Innovative Plastics Noryl N190HX PPE+PS 物性表
| 比重 | 1.10 g/cc | 1.10 g/cc | ASTM D 792 |
| 吸水率 | 0.066 % @Time 86400 sec | 0.066 % @Time 24.0 hour | ASTM D 570 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| 洛氏硬度（R 级） | 117 | 117 | ASTM D 785 |
| 抗张强度(断裂) | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D 638 |
| 抗张强度(屈服) | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D 638 |
| 伸长率 (断裂) | 14 % | 14 % | Type I, 50 mm/min; ASTM D 638 |
| 屈服伸长率 | 3.8 % | 3.8 % | Type I, 50 mm/min; ASTM D 638 |
| 拉伸模量 | 2.46 GPa | 357 ksi | 50 mm/min; ASTM D 638 |
| 弯曲强度 | 89.0 MPa | 12900 psi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| 弯曲模量 | 2.27 GPa | 329 ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| 悬壁梁缺口冲击强度 | 0.800 J/cm @Temperature -30.0 °C | 1.50 ft-lb/in @Temperature -22.0 °F | ASTM D 256 |
| 1.92 J/cm @Temperature 23.0 °C | 3.60 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |
| 悬壁梁无缺口冲击强度 | 18.69 J/cm @Temperature 23.0 °C | 35.01 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| 冲击试验 | 11.0 J @Temperature -30.0 °C | 8.11 ft-lb @Temperature -22.0 °F | Instrumented Impact Energy @ peak; ASTM D 3763 |
| 37.0 J @Temperature 23.0 °C | 27.3 ft-lb @Temperature 73.4 °F | Instrumented Impact Energy @ peak; ASTM D 3763 | |
| 泰伯磨损，毫克/1000次 | 82 @Load 1.00 kg | 82 @Load 2.20 lb | CS-17; ASTM D 1044 |
| 体积电阻率 | 8.00e+16 ohm-cm | 8.00e+16 ohm-cm | ASTM D 257 |
| 表面电阻 | >= 1.00e+11 ohm | >= 1.00e+11 ohm | ASTM D 257 |
| 介电常数 | 2.6 @Frequency 100000 Hz | 2.6 @Frequency 100000 Hz | ASTM D 150 |
| 介电强度 | 28.1 kV/mm @Thickness 1.60 mm | 714 kV/in @Thickness 0.0630 in | in oil; ASTM D 149 |
| 耗散因数 | 0.0057 @Frequency 100000 Hz | 0.0057 @Frequency 100000 Hz | ASTM D 150 |
| 0.011 @Frequency 100 Hz | 0.011 @Frequency 100 Hz | ASTM D 150 | |
| 耐电弧性 | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten, PLC code 7; ASTM D 495 |
| 相比耐漏电起痕指数(CTI) | 400 - 600 V | 400 - 600 V | PLC code 1; UL 746A |
| 热丝引燃 (HWI) | 30 - 60 sec | 30 - 60 sec | PLC code 2; UL 746A |
| 高电弧燃烧，HAI | 30 - 60 arcs | 30 - 60 arcs | surface, PLC code 2; UL 746A |
| 高压电弧跟踪率，HVTR | >= 150 mm/min | >= 5.91 in/min | PLC code 4; UL 746A |
| 线形热膨胀系数 - 流动 | 90.0 µm/m-°C @Temperature -40.0 - 95.0 °C | 50.0 µin/in-°F @Temperature -40.0 - 203 °F | ASTM E 831 |
| 线性热膨胀系数,横向流动 | 91.8 µm/m-°C @Temperature -40.0 - 95.0 °C | 51.0 µin/in-°F @Temperature -40.0 - 203 °F | ASTM E 831 |
| 导热系数 | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | ASTM C 177 |
| 载荷下热变形温度(0.46 MPa) | 95.0 °C @Thickness 6.40 mm | 203 °F @Thickness 0.252 in | unannealed; ASTM D 648 |
| 载荷下热变形温度(1.8 MPa) | 83.0 °C @Thickness 6.40 mm | 181 °F @Thickness 0.252 in | unannealed; ASTM D 648 |
| UL RTI | 95.0 °C | 203 °F | UL 746B |
| UL RTI，机械冲击 | 80.0 °C | 176 °F | UL 746B |
| UL RTI，机械无冲击 | 95.0 °C | 203 °F | UL 746B |
| 可燃性(UL94) | HB @Thickness 1.01 mm | HB @Thickness 0.0398 in | UL 94 |
| V-0 @Thickness 1.47 mm | V-0 @Thickness 0.0579 in | UL 94 | |
| 5VA @Thickness 2.99 mm | 5VA @Thickness 0.118 in | UL 94 | |
| 极限氧指数 | 35.7 % | 35.7 % | LOI; ASTM D 2863 |
| Radiant Panel Listing | YES | UL Tested |
| UV-light, water exposure/immersion | F1 | UL 746C |