汽车部件用料PPO 沙伯基础PPOGTX974 耐高温可喷涂PPO
SABIC Innovative Plastics NORYL GTX GTX974 PPE+PA
Polyphenylene Ether/PPO
SABIC Innovative Plastics (GE Plastics)
产品说明：
NORYL GTX974 is a material especially designed for in- or on-line painted bodypanels and fenders in particular. This material combines impact performance with conductivity for electro-static painting in an unique way.
物性信息：
| 比重 | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| 密度 | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| 水分吸收 | 1.20 % | 1.20 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 4.2 % | 4.2 % | ISO 62 |
| 线性成型收缩率,Flow | 0.013 - 0.016 cm/cm @Thickness 3.20 mm | 0.013 - 0.016 in/in @Thickness 0.126 in | SABIC Method |
| 线性成型收缩率，横向 | 0.011 - 0.014 cm/cm @Thickness 3.20 mm | 0.011 - 0.014 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 10 g/10 min @Load 5.00 kg, Temperature 280 °C | 10 g/10 min @Load 11.0 lb, Temperature 536 °F | ASTM D1238 |
| 化合物熔体指数 | 12 g/10 min @Load 5.00 kg, Temperature 280 °C | 12 g/10 min @Load 11.0 lb, Temperature 536 °F | MVR [cm^3/10 min]; ISO 1133 |
| 抗张强度(断裂) | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 | |
| 抗张强度(屈服) | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
| 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 | |
| 伸长率 (断裂) | 30 % | 30 % | 50 mm/min; ISO 527 |
| 50 % | 50 % | Type I, 50 mm/min; ASTM D638 | |
| 屈服伸长率 | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 | |
| 拉伸模量 | 2.00 GPa | 290 ksi | 1 mm/min; ISO 527 |
| 2.05 GPa | 297 ksi | 50 mm/min; ASTM D638 | |
| 弯曲强度 | 75.0 MPa | 10900 psi | 2 mm/min; ISO 178 |
| 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
| 2.05 GPa | 297 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 悬壁梁缺口冲击强度 | 1.80 J/cm | 3.37 ft-lb/in | ASTM D256 |
| 1.20 J/cm @Temperature -30.0 °C | 2.25 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 17.0 kJ/m² | 8.09 ft-lb/in² | 80*10*4; ISO 180/1A | |
| 10.0 kJ/m² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| 简支梁缺口冲击强度 | 1.80 J/cm² | 8.57 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| 落锤总能量 | 50.0 J @Temperature 23.0 °C | 36.9 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| 体积电阻率 | 1000 - 10000 ohm-cm | 1000 - 10000 ohm-cm | SABIC Method |
| 线形热膨胀系数 - 流动 | 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 50.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 100 µm/m-°C @Temperature 23.0 - 60.0 °C | 55.6 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | 90.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 50.0 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| 100 µm/m-°C @Temperature -40.0 - 40.0 °C | 55.6 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| 载荷下热变形温度(0.46 MPa) | 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 180 °C @Thickness 3.20 mm | 356 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 维卡软化温度 | 175 °C | 347 °F | Rate B/50; ISO 306 |
| 180 °C | 356 °F | Rate B/120; ISO 306 | |
| 180 °C | 356 °F | Rate B/50; ASTM D1525 | |
| 230 °C | 446 °F | Rate A/50; ISO 306 | |
| 可燃性(UL94) | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL 94 |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | UL 94 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |