电气绝缘件PPO 沙伯基础PPOV01525 低翘曲PPO 性能沙特基础NORYL™PPE+PSV01525

>(PPE+PS)-MGF15-FR< 阻燃等级: V-1 • V-0 • 5VA 比重: 1.13 g/cm³ 缺口冲击: 5.10 kJ/m² 符合规定: UL材料特性: 尺寸稳定 • 低翘曲材料用途: 电器内部构件 • 电气外壳面板 • 电气绝缘件 • 外壳

PPO沙伯基础2.jpg

电气性能额定值 (公制)额定值 (英制)测试方法
体积电阻率1.00e+15 ohm-cm1.00e+15 ohm-cmIEC 60093
表面电阻>= 1.00e+15 ohm>= 1.00e+15 ohmROA; IEC 60093
介电常数2.9

@Frequency 1.00e+6 Hz

2.9

@Frequency 1.00e+6 Hz

IEC 60250

3.0

@Frequency 50.0 - 60.0 Hz

3.0

@Frequency 50.0 - 60.0 Hz

IEC 60250
介电强度16.0 kV/mm

@Thickness 3.20 mm

406 kV/in

@Thickness 0.126 in

in oil; IEC 60243-1

26.0 kV/mm

@Thickness 1.60 mm

660 kV/in

@Thickness 0.0630 in

in oil; IEC 60243-1

33.0 kV/mm

@Thickness 0.800 mm

838 kV/in

@Thickness 0.0315 in

in oil; IEC 60243-1
耗散因数0.0030

@Frequency 1.00e+6 Hz

0.0030

@Frequency 1.00e+6 Hz

IEC 60250

0.0060

@Frequency 50.0 - 60.0 Hz

0.0060

@Frequency 50.0 - 60.0 Hz

IEC 60250
相比耐漏电起痕指数(CTI)175 V175 VIEC 60112
热性能额定值 (公制)额定值 (英制)测试方法
线形热膨胀系数 - 流动50.0 µm/m-°C

@Temperature 23.0 - 80.0 °C

27.8 µin/in-°F

@Temperature 73.4 - 176 °F

ISO 11359-2

66.0 µm/m-°C

@Temperature -40.0 - 40.0 °C

36.7 µin/in-°F

@Temperature -40.0 - 104 °F

ASTM E 831
线性热膨胀系数,横向流动52.0 µm/m-°C

@Temperature -40.0 - 40.0 °C

28.9 µin/in-°F

@Temperature -40.0 - 104 °F

ASTM E 831

60.0 µm/m-°C

@Temperature 23.0 - 80.0 °C

33.3 µin/in-°F

@Temperature 73.4 - 176 °F

ISO 11359-2
导热系数0.280 W/m-K1.94 BTU-in/hr-ft²-°FISO 8302
Hot Ball Pressure Test<= 125 °C<= 257 °FIEC 60695-10-2
载荷下热变形温度(1.8 MPa)115 °C239 °FEdgew 120*10*4 sp=100mm; ISO 75/Ae

120 °C

@Thickness 3.20 mm

248 °F

@Thickness 0.126 in

unannealed; ASTM D648
维卡软化温度130 °C266 °FRate B/50; ISO 306

140 °C284 °FRate B/120; ISO 306

140 °C284 °FRate B/50; ASTM D1525

140 °C284 °FRate A/50; ISO 306
UL RTI50.0 °C122 °FUL 746B
UL RTI,机械冲击50.0 °C122 °FUL 746B
UL RTI,机械无冲击50.0 °C122 °FUL 746B
可燃性(UL94)V-1

@Thickness 1.20 mm

V-1

@Thickness 0.0472 in

UL 94

V-0

@Thickness 1.50 mm

V-0

@Thickness 0.0591 in

UL 94

5VA

@Thickness 3.00 mm

5VA

@Thickness 0.118 in

UL 94
极限氧指数32 %32 %ISO 4589
灼热丝试验960 °C

@Thickness 3.20 mm

1760 °F

@Thickness 0.126 in

IEC 60695-2-12