美国杜邦 PA66 70G30HSL 30%玻璃纤维增强材料
70G30HSL 产品说明：
30% Glass Reinforced Heat Stabilized Polyamide 66
Zytel 70G30HSL NC010 is a 30% glass fiber reinforced heat stabilized polyamide 66 resin for injection molding.
Information provided by DuPont Performance Polymers
物性信息：
| 密度 | 1.37 g/cc | 0.0495 lb/in³ | DAM; ISO 1183 |
| 吸水率 | 6.0 % @Thickness 2.00 mm | 6.0 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 水分吸收 | 1.90 % @Thickness 2.00 mm | 1.90 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 粘度 | 46970 cP @Shear Rate 5000 1/s, Temperature 305 °C | 46970 cP @Shear Rate 5000 1/s, Temperature 581 °F | ISO 11403-1 -2 |
| 58620 cP @Shear Rate 5000 1/s, Temperature 295 °C | 58620 cP @Shear Rate 5000 1/s, Temperature 563 °F | ISO 11403-1 -2 | |
| 74567 cP @Shear Rate 5000 1/s, Temperature 285 °C | 74567 cP @Shear Rate 5000 1/s, Temperature 545 °F | ISO 11403-1 -2 | |
| 119700 cP @Shear Rate 500 1/s, Temperature 305 °C | 119700 cP @Shear Rate 500 1/s, Temperature 581 °F | ISO 11403-1 -2 | |
| 154240 cP @Shear Rate 500 1/s, Temperature 295 °C | 154240 cP @Shear Rate 500 1/s, Temperature 563 °F | ISO 11403-1 -2 | |
| 201130 cP @Shear Rate 500 1/s, Temperature 285 °C | 201130 cP @Shear Rate 500 1/s, Temperature 545 °F | ISO 11403-1 -2 | |
| 线性成型收缩率,Flow | 0.0030 cm/cm | 0.0030 in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | 0.011 cm/cm | 0.011 in/in | DAM; ISO 294-4 2577 |
| 洛氏硬度（M 级） | 88 | 88 | 50%RH; ISO 2039-2 |
| 104 | 104 | DAM; ISO 2039-2 | |
| 洛氏硬度（R 级） | 117 | 117 | 50%RH; ISO 2039-2 |
| 124 | 124 | DAM; ISO 2039-2 | |
| 抗张强度(断裂) | 130 MPa | 18900 psi | 50%RH; ISO 527-1/-2 |
| 200 MPa | 29000 psi | DAM; ISO 527-1/-2 | |
| 伸长率 (断裂) | 3.4 % | 3.4 % | DAM; ISO 527-1/-2 |
| 5.0 % | 5.0 % | 50%RH; ISO 527-1/-2 | |
| 拉伸模量 | 7.00 GPa | 1020 ksi | 50%RH; ISO 527-1/-2 |
| 10.0 GPa | 1450 ksi | DAM; ISO 527-1/-2 | |
| 剪切模量 | 0.6452 GPa @Temperature 150 °C | 93.58 ksi @Temperature 302 °F | DAM; Dynamic; ISO 11403-1 -2 |
| 0.714 GPa @Temperature 110 °C | 104 ksi @Temperature 230 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| 1.2377 GPa @Temperature 60.0 °C | 179.52 ksi @Temperature 140 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| 1.8948 GPa @Temperature 10.0 °C | 274.82 ksi @Temperature 50.0 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| 1.9612 GPa @Temperature -20.0 °C | 284.45 ksi @Temperature -4.00 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| 2.0275 GPa @Temperature -50.0 °C | 294.07 ksi @Temperature -58.0 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| 悬壁梁缺口冲击强度 | 13.0 kJ/m² | 6.19 ft-lb/in² | DAM; ISO 180/1A |
| 17.0 kJ/m² | 8.09 ft-lb/in² | 50%RH; ISO 180/1A | |
| 10.0 kJ/m² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 180/1A | |
| 12.0 kJ/m² @Temperature -30.0 °C | 5.71 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | |
| 简支梁无缺口冲击强度 | 8.20 J/cm² | 39.0 ft-lb/in² | DAM; ISO 179/1eU |
| 9.30 J/cm² | 44.3 ft-lb/in² | 50%RH; ISO 179/1eU | |
| 7.00 J/cm² @Temperature -30.0 °C | 33.3 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | |
| 7.30 J/cm² @Temperature -30.0 °C | 34.7 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 1.20 J/cm² | 5.71 ft-lb/in² | DAM; ISO 179/1eA |
| 1.60 J/cm² | 7.61 ft-lb/in² | 50%RH; ISO 179/1eA | |
| 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |
| 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | |
| 拉伸蠕变模量(1 hr) | 6800 MPa @Time 3600 sec | 986000 psi @Time 1.00 hour | 50%RH; ISO 899-1 |
| 拉伸蠕变模量(1000 hr) | 5100 MPa @Time 3.60e+6 sec | 740000 psi @Time 1000 hour | 50%RH; ISO 899-1 |
| 体积电阻率 | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | 50%RH; IEC 60093 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | DAM; IEC 60093 | |
| 表面电阻 | 1.00e+13 ohm | 1.00e+13 ohm | 50%RH; IEC 60093 |
| 1.00e+15 ohm | 1.00e+15 ohm | DAM; ASTM D257 | |
| 介电常数 | 4.1 @Frequency 1.00e+6 Hz | 4.1 @Frequency 1.00e+6 Hz | DAM; IEC 60250 |
| 4.4 @Frequency 100 Hz | 4.4 @Frequency 100 Hz | DAM; IEC 60250 | |
| 4.6 @Frequency 1.00e+6 Hz | 4.6 @Frequency 1.00e+6 Hz | 50%RH; IEC 60250 | |
| 10.8 @Frequency 100 Hz | 10.8 @Frequency 100 Hz | 50%RH; IEC 60250 | |
| 介电强度 | 32.0 kV/mm | 813 kV/in | 50%RH; IEC 60243-1 |
| 38.0 kV/mm | 965 kV/in | DAM; IEC 60243-1 | |
| 耗散因数 | 0.0070 @Frequency 100 Hz | 0.0070 @Frequency 100 Hz | DAM; IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz | 0.015 @Frequency 1.00e+6 Hz | DAM; IEC 60250 | |
| 0.065 @Frequency 1.00e+6 Hz | 0.065 @Frequency 1.00e+6 Hz | 50%RH; IEC 60250 | |
| 0.46 @Frequency 100 Hz | 0.46 @Frequency 100 Hz | 50%RH; IEC 60250 | |
| 相比耐漏电起痕指数(CTI) | 400 V | 400 V | DAM; IEC 60112 |
| 线形热膨胀系数 - 流动 | 22.0 µm/m-°C | 12.2 µin/in-°F | DAM; ISO 11359-1/-2 |
| 线性热膨胀系数,横向流动 | 107 µm/m-°C | 59.4 µin/in-°F | DAM; ISO 11359-1/-2 |
| 熔融温度 | 263 °C | 505 °F | DAM; 10°C/min; ISO 11357-1/-3 |
| 载荷下热变形温度(0.46 MPa) | 261 °C | 502 °F | DAM; ISO 75-1/-2 |
| 载荷下热变形温度(1.8 MPa) | 248 °C | 478 °F | DAM; ISO 75-1/-2 |
| 可燃性(UL94) | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 |
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | DAM; IEC 60695-11-10 | |
| Flame Spread | 13 mm/min @Thickness 1.00 mm | 0.51 in/min @Thickness 0.0394 in | ISO 3795 (FMVSS 302) |
| 部件标识代码 | >PA66-GF30< | ISO 11469 |
| 加工 | Injection Moulding | |
| 供货地区 | Europe | |
| Near East/Africa | ||
| 树脂识别 | PA66-GF30 | |
| 特殊特性 | Heat stabilised or stable to heat | |
| UL recognition | UL | DAM |