供应10%玻纤 PBT 美国杜邦 T835FRUV-NC010
DuPont Performance Polymers Crastin® T835FRUV NC010 PBT
Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled
DuPont Performance Polymers
产品说明：
Crastin® T835FRUV NC010 is a 5% glass fiber reinforced, toughened, flame retardant polybutylene terephthalate resin for injection molding. (precommercial code = Crastin® CE2402)
Information provided by DuPont Performance Polymers
物性信息：
| 密度 | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| 填料含量 | 5.0 % | 5.0 % | |
| 线性成型收缩率 | 0.013 cm/cm @Thickness 3.20 mm | 0.013 in/in @Thickness 0.126 in | Transverse |
| 0.014 cm/cm @Thickness 3.20 mm | 0.014 in/in @Thickness 0.126 in | Flow |
| 抗张强度(断裂) | 60.0 MPa @Temperature 23.0 °C | 8700 psi @Temperature 73.4 °F | ASTM D638 |
| 62.0 MPa @Temperature 23.0 °C | 8990 psi @Temperature 73.4 °F | ISO 527 | |
| 伸长率 (断裂) | 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | ASTM D638 |
| 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | ISO 527 | |
| 拉伸模量 | 3.40 GPa @Temperature 23.0 °C | 493 ksi @Temperature 73.4 °F | ISO 527 |
| 弯曲模量 | 3.10 GPa @Temperature 23.0 °C | 450 ksi @Temperature 73.4 °F | ISO 178 |
| 3.20 GPa @Temperature 23.0 °C | 464 ksi @Temperature 73.4 °F | ASTM D790 | |
| 悬壁梁缺口冲击强度 | 1.50 J/cm @Temperature 23.0 °C | 2.81 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| 9.00 kJ/m² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |
| 悬壁梁无缺口冲击强度 | 45.0 kJ/m² @Temperature 23.0 °C | 21.4 ft-lb/in² @Temperature 73.4 °F | ISO 180/1U |
| 简支梁无缺口冲击强度 | 5.50 J/cm² @Temperature 23.0 °C | 26.2 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU |
| 简支梁缺口冲击强度 | 0.900 J/cm² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA |
| 熔融温度 | 223 °C | 433 °F | 10°C/min; ISO 11357-1/-3 |
| 载荷下热变形温度(1.8 MPa) | 120 °C | 248 °F | ISO 75-1/-2 |
| UL RTI | 130 °C @Thickness 0.800 mm | 266 °F @Thickness 0.0315 in | UL 746B |
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | |
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | |
| UL RTI，机械冲击 | 130 °C @Thickness 0.800 mm | 266 °F @Thickness 0.0315 in | UL 746B |
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | |
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | |
| UL RTI，机械无冲击 | 130 °C @Thickness 0.800 mm | 266 °F @Thickness 0.0315 in | UL 746B |
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | |
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | |
| 可燃性(UL94) | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | IEC 60695-11-10 |
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | IEC 60695-11-10 | |
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | IEC 60695-11-10 | |
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | UL94 | |
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL94 | |
| V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | UL94 |