刚性良好 POM 德国巴斯夫 S1320-003 薄壁部件原料
![](http://static.11467.com/img/ab-prev-0.png)
![](http://img.11467.com/2021/05-18/4139151068_small.jpg)
![](http://img.11467.com/2021/05-18/4139151068_small.jpg)
![](http://img.11467.com/2024/05-16/1560115359_small.jpg)
![](http://img.11467.com/2021/05-18/4521715606_small.jpg)
![](http://img4.11467.com/2021/12-06/1234540369_small.jpg)
![](http://static.11467.com/img/ab-next-0.png)
更新时间:2024-07-01 07:00:00
价格:请来电询价
品牌:德国巴斯夫
型号:S1320-003
性能:刚性良好 共聚物 良好的流动性
联系电话:
联系手机:13532886152
联系人:汪修建
让卖家联系我
详细介绍
Ultraform® S 1320 003
Acetal (POM) Copolymer
BASF Corporation
产品说明:
Free-flowing, rapidly solidifying grade for moldings difficult to produce by injection molding and having low wall thickness; increased stiffness and heat distortion resistance.
物性信息:
黄卡编号 |
|
特性 |
|
用途 |
|
机构评级 |
|
RoHS 合规性 |
|
形式 |
|
加工方法 |
|
多点数据 |
|
树脂ID (ISO 1043) |
|
密度 | 1.41 | g/cm³ | ISO 1183 |
表观密度 | 0.85 | g/cm³ | |
溶化体积流率(MVR) (190°C/2.16 kg) | 11.0 | cm³/10min | ISO 1133 |
收缩率 | ISO 294-4 | ||
垂直流动方向 | 2.1 | % | ISO 294-4 |
流动方向 | 2.1 | % | ISO 294-4 |
吸水率 | ISO 62 | ||
饱和, 23°C | 0.80 | % | ISO 62 |
平衡, 23°C, 50% RH | 0.20 | % | ISO 62 |
球压硬度 (H 358/30) | 165 | MPa | ISO 2039-1 |
拉伸模量 | 3000 | MPa | ISO 527-2 |
拉伸应力 (屈服) | 68.0 | MPa | ISO 527-2/50 |
拉伸应变 (屈服) | 9.0 | % | ISO 527-2/50 |
标称拉伸断裂应变 | 25 | % | ISO 527-2/50 |
拉伸蠕变模量 1(1000 hr) | 1450 | MPa | ISO 899-1 |
简支梁缺口冲击强度 | ISO 179/1eA | ||
-30°C | 5.5 | kJ/m² | ISO 179/1eA |
23°C | 5.5 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 | ISO 179/1eU | ||
-30°C | 170 | kJ/m² | ISO 179/1eU |
23°C | 170 | kJ/m² | ISO 179/1eU |
热变形温度 (1.8 MPa, 未退火) | 100 | °C | ISO 75-2/A |
熔融温度 | 171 | °C | ISO 11357-3 |
线形热膨胀系数 - 流动 (23 到 55°C) | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
Zui高使用温度 - short cycle operation | 100 | °C |
Automotive Materials (> 1.00 mm) | Passed | FMVSS 302 | |
ISO Type | POM-K, M-GNR, 04-002 | ISO 9988-1 |
Screw Speed | mm/sec |
表面电阻率 | 1.0E+15 | ohms | IEC 60093 |
体积电阻率 | 1.0E+15 | ohms·cm | IEC 60093 |
相对电容率 (1 MHz) | 3.70 | IEC 60250 | |
耗散因数 (1 MHz) | 5.0E-3 | IEC 60250 | |
漏电起痕指数 (解决方案 A) | 600 | V | IEC 60112 |
UL 阻燃等级 (1.60 mm) | HB | UL 94 |
干燥温度 | 100 | °C | |
干燥时间 | 3.0 | hr | |
建议的Zui大水分含量 | 0.20 | % | |
料斗温度 | 200 | °C | |
料筒后部温度 | 200 | °C | |
料筒中部温度 | 200 | °C | |
料筒前部温度 | 200 | °C | |
射嘴温度 | 200 | °C | |
加工(熔体)温度 | 190 到 230 | °C | |
模具温度 | 60.0 到 120 | °C |