LEXAN™ PC 基础创新(美国) 925AU 抗紫外线 阻燃
![](http://static.11467.com/img/ab-prev-0.png)
![](http://img.11467.com/2021/04-15/3847384259_small.jpg)
![](http://img.11467.com/2021/04-15/3847384259_small.jpg)
![](http://img.11467.com/2024/06-07/3211764304_small.jpg)
![](http://img.11467.com/2024/06-12/4394080302_small.jpg)
![](http://img.11467.com/2024/06-07/3295770843_small.jpg)
![](http://static.11467.com/img/ab-next-0.png)
更新时间:2024-07-06 07:00:00
价格:请来电询价
品牌:基础创新(美国)
型号:925AU
性能:紫外线稳定剂 阻燃性
联系电话:
联系手机:13532886152
联系人:汪修建
让卖家联系我
详细介绍
LEXAN™ 925AU resin
物性信息:
黄卡编号 |
|
添加剂 |
|
特性 |
|
用途 |
|
外观 |
|
加工方法 |
|
![PC沙特.jpg PC沙特.jpg](http://img4.11467.com/2020/12-03/1135087225.jpg)
比重 | 1.19 | g/cm³ | ASTM D792 |
熔流率(熔体流动速率) (300°C/1.2 kg) | 13 | g/10 min | ASTM D1238 |
收缩率 - 流动 (3.20 mm) | 0.60 到 0.80 | % | 内部方法 |
室外适用性 | f1 | UL 746C |
拉伸模量 1 | 2270 | MPa | ASTM D638 |
抗张强度 2 | ASTM D638 | ||
屈服 | 62.0 | MPa | ASTM D638 |
断裂 | 67.0 | MPa | ASTM D638 |
伸长率 3 | ASTM D638 | ||
屈服 | 6.0 | % | ASTM D638 |
断裂 | 130 | % | ASTM D638 |
弯曲模量 4(50.0 mm 跨距) | 2370 | MPa | ASTM D790 |
弯曲强度 5(屈服, 50.0 mm 跨距) | 101 | MPa | ASTM D790 |
![PC上海拜耳-1.jpg PC上海拜耳-1.jpg](http://img.11467.com/2021/06-29/1325829627.jpg)
悬壁梁缺口冲击强度 (23°C) | 800 | J/m | ASTM D256 |
装有测量仪表的落镖冲击 (23°C, Total Energy) | 79.0 | J | ASTM D3763 |
载荷下热变形温度 | ASTM D648 | ||
0.45 MPa, 未退火, 3.20 mm | 137 | °C | ASTM D648 |
1.8 MPa, 未退火, 3.20 mm | 126 | °C | ASTM D648 |
维卡软化温度 | 143 | °C | ASTM D1525 6 |
线形热膨胀系数 | ASTM E831 | ||
流动 : -40 到 40°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
横向 : -40 到 40°C | 7.4E-5 | cm/cm/°C | ASTM E831 |
RTI Elec | 130 | °C | UL 746 |
RTI Imp | 120 | °C | UL 746 |
RTI | 130 | °C | UL 746 |
耐电弧性 7 | PLC 7 | ASTM D495 | |
相比耐漏电起痕指数(CTI) | PLC 3 | UL 746 | |
高电弧燃烧指数(HAI) | PLC 2 | UL 746 | |
高电压电弧起痕速率 (HVTR) | PLC 3 | UL 746 | |
热丝引燃 (HWI) | PLC 2 | UL 746 |
UL 阻燃等级 | UL 94 | ||
0.800 mm | V-2 | UL 94 | |
3.04 mm | V-0 | UL 94 | |
灼热丝易燃指数 (1.00 mm) | 960 | °C | IEC 60695-2-12 |
热灯丝点火温度 (1.00 mm) | 850 | °C | IEC 60695-2-13 |
干燥温度 | 120 | °C | |
干燥时间 | 2.0 到 4.0 | hr | |
建议的Zui大水分含量 | 0.020 | % | |
料斗温度 | 60.0 到 80.0 | °C | |
料筒后部温度 | 260 到 280 | °C | |
料筒中部温度 | 270 到 290 | °C | |
料筒前部温度 | 280 到 310 | °C | |
射嘴温度 | 270 到 290 | °C | |
加工(熔体)温度 | 280 到 310 | °C | |
模具温度 | 80.0 到 110 | °C |