PA9T G1300H日本可乐丽G1300H

产品说明

The G1300H and G1350H are suitable for use in a wide range of electrical and electronics components as UL94 HB flammability rating, while the

G1302 grade delivers low friction. HB grades do not contain halogen-containing flame-retardants. The GW1458HF offers low warpage and high

flow-ability.

*'Halogen free' follows the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than

1500ppm.

总体

材料状态• 已商用：当前有效

资料 1 • Technical Datasheet (English)

UL 黄卡 2 • E90350-252511

搜索UL 黄卡• Kuraray Co., Ltd.

• Genestar™

填料/增强材料• 玻璃纤维增强材料, 30% 填料按重量

特性• 无卤

用途• 电气/电子应用领域• 电气元件

物理性能额定值单位制测试方法

比重1.37 g/cm³

熔流率（熔体流动速率） (320°C/2.16 kg) 45 g/10 min ASTM D1238

收缩率

流动: 1.00 mm 0.20 %

横向流动: 1.00 mm 0.80 %

吸水率 4 (平衡, 40°C, 95%RH) 1.6 %

机械性能额定值单位制测试方法

抗张强度160 MPa ASTM D638

伸长率(断裂) 4.0 % ASTM D638

弯曲模量8500 MPa ASTM D790

弯曲强度205 MPa ASTM D790

冲击性能额定值单位制测试方法

悬壁梁缺口冲击强度110 J/m ASTM D256

热性能额定值单位制测试方法

载荷下热变形温度(1.8 MPa, 未退火) 290 °C ASTM D648

玻璃转化温度125 °C

熔融温度306 °C