PPS1140E7 电气性能额定值单位制测试方法
表面电阻率> 1.0E+15 ohm IEC 60093
体积电阻率
-- 1.0E+17 ohm·cm ASTM D257
-- > 1.0E+15 ohm·cm IEC 60093
耐电强度25 kV/mm IEC 60243-1
介电常数
1 kHz 3.70 ASTM D150
1 MHz 3.70 ASTM D150
1 MHz 4.70 IEC 60250
耗散因数
1 kHz 1.0E-3 ASTM D150
1 MHz 1.0E-3 ASTM D150
1 MHz 0.020 IEC 60250
耐电弧性134 sec ASTM D495
可燃性额定值单位制测试方法
UL 阻燃等级UL 94
0.850 mm V-0
1.50 mm V-0
极限氧指数47 % ASTM D2863
ISO 4589-2
补充信息额定值单位制测试方法
Specimen Thickness - Shrinkage 3.18 mm 内部方法
注射额定值单位制
干燥温度130 到140 °C
干燥时间3.0 到4.0 hr
建议的Zui大水分含量0.020 %
料筒温度20.0 到30.0 °C
螺筒后部温度290 到300 °C
螺筒中部温度310 到320 °C
热性能额定值单位制测试方法
热变形温度
0.45 MPa, 退火280 °C ASTM D648
1.8 MPa, 未退火270 °C ASTM D648
ISO 75-2/A
8.0 MPa, 未退火215 °C ISO 75-2/C
玻璃转化温度 5 90.0 °C ISO 11357-2
熔融温度
-- 5 280 °C ISO 11357-3
-- 282 °C ASTM D3418
线形膨胀系数ISO 11359-2
流动2.0E-5 cm/cm/°C
横向4.1E-5 cm/cm/°C