CYCOLOY™ MC8002 resin 物性表
| 特性 |
|
| 用途 |
|
| 加工方法 |
|
| 多点数据 |
|
| 比重 | 1.14 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (260°C/5.0 kg) | 9.0 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 (3.20 mm) | 0.50 到 0.70 | % | 内部方法 |
| 吸水率 | ASTM D570 | ||
| 24 hr | 0.10 | % | ASTM D570 |
| 平衡, 23°C | 0.40 | % | ASTM D570 |
| 拉伸模量 1 | 2210 | MPa | ASTM D638 |
| 抗张强度 2(屈服) | 56.5 | MPa | ASTM D638 |
| 伸长率 3 | ASTM D638 | ||
| 屈服 | 5.0 | % | ASTM D638 |
| 断裂 | 150 | % | ASTM D638 |
| 弯曲模量 4(50.0 mm 跨距) | 2340 | MPa | ASTM D790 |
| 弯曲强度 5(屈服, 50.0 mm 跨距) | 86.2 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 | ASTM D256 | ||
| -30°C | 530 | J/m | ASTM D256 |
| 23°C | 640 | J/m | ASTM D256 |
| 装有测量仪表的落镖冲击 | ASTM D3763 | ||
| -30°C, Total Energy | 54.2 | J | ASTM D3763 |
| 23°C, Total Energy | 61.0 | J | ASTM D3763 |
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 3.20 mm | 124 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 3.20 mm | 107 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm | 110 | °C | ASTM D648 |
| 线形热膨胀系数 - 流动 (-40 到 40°C) | 7.2E-5 | cm/cm/°C | ASTM E831 |
| 导热系数 | 0.20 | W/m/K | ASTM C177 |
| 干燥温度 | 104 到 110 | °C | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 干燥时间， | 8.0 | hr | |
| 建议的水分含量 | 0.040 | % | |
| 建议注射量 | 30 到 80 | % | |
| 料筒后部温度 | 249 到 288 | °C | |
| 料筒中部温度 | 254 到 293 | °C | |
| 料筒前部温度 | 260 到 302 | °C | |
| 射嘴温度 | 274 到 302 | °C | |
| 加工（熔体）温度 | 274 到 302 | °C | |
| 模具温度 | 60 到 88 | °C | |
| 背压 | 0.345 到 0.689 | MPa | |
| 螺杆转速 | 40 到 70 | rpm | |
| 排气孔深度 | 0.038 到 0.076 | mm |